Título: Effect of crystallographic orientations on the hydrogen-induced cracking resistance improvement of API 5L X70 pipeline steel under various thermomechanical processing
Autor(es): Masoumi, Mohammad
Silva, Cleiton Carvalho
Abreu, Hamilton Ferreira Gomes de
Palavras-chave: API 5L X70 steel
Crystallographic texture
Thermomechanical processing
Hydrogen-induced cracking
Ciência dos materiais
Termomecânica
Fissura (Engenharia Civil)
Aço - Resistência
Resistência de materiais
Data do documento: 4-Mai-2016
Editor: Corrosion Science
Citação: MASOUMI, M. ; SILVA, C. C. ; ABREU, H. F. G. (2016)
Abstract: In this study a thermomechanical processing was suggested to improve the hydrogen-induced cracking(HIC) resistance in X70 pipeline steel. Proposed thermomechanical treatment produced favorable crys-tallographic textures and significantly increased HIC resistance which is of great interest to petroleumindustry. The results showed that the high angle grain boundaries and Kernel parameter values acted ashydrogen-trapping sites, leading to increased HIC susceptibility. Highest HIC resistance was obtained insample rolled isothermally at 850◦C, due to the high proportion of grains oriented with {110} planes par-allel to the normal direction and {111}//ND fibers accompanied by negligible fraction of grains orientedin {001}//ND.
Descrição: MASOUMI, M.; SILVA, C. C.; ABREU, H. F. G. Effect of crystallographic orientations on the hydrogen-induced cracking resistance improvement of API 5L X70 pipeline steel under various thermomechanical processing. Corrosion Science, v. 12, n. 111, p. 121-31. 2016.
URI: http://www.repositorio.ufc.br/handle/riufc/22462
ISSN: 0010-938X
Aparece nas coleções:DEMM - Artigos publicados em revista científica

Arquivos associados a este item:
Arquivo Descrição TamanhoFormato 
2016_art_hfgabreu_effect.pdf7,1 MBAdobe PDFVisualizar/Abrir


Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.