Título: Influência da adição de cargas inorgânicas no desempenho de produtos refratários obtidos a partir de borras de alumínio
Título em inglês: Influence of addition of inorganic fillers on the performance of refractory products made ​​from aluminum sludge
Autor(es): Mota, Rejane Carneiro
Orientador(es): Nogueira, Ricardo Emílio Ferreira Quevedo
Coorientador(es): Sasaki, José Marcos
Palavras-chave: Alumínio
Materiais refratários
Moagem (Beneficiamento de minério)
Ciência dos materiais
Data do documento: Nov-2010
Citação: MOTA, R. C. (2010)
Resumo: A borra branca é um resíduo gerado durante a produção do alumínio, que contém óxidos que podem ser utilizados na indústria dos refratários e cimentos. A borra de alumínio, se não for inertizada, é perigosa para a saúde humana e contaminante do meio ambiente. Neste trabalho, a borra de alumínio foi submetida a tratamento térmico seguido de moagem e classificação por peneiramento. Para melhorar as propriedades mecânicas das peças obtidas a partir da borra de alumínio, foram formuladas duas misturas com adição de partículas de reforço inorgânicas eletrofundidas. Neste caso, a mulita do tipo TP-325, com porcentagens variando entre 5 e 35% e a outra com alumina do tipo AL-L 280 variando entre 20 e 30% em peso, sendo comparadas com a borra pura (matriz cerâmica). O resíduo e as cargas inorgânicas foram caracterizados por fluorescência de raios x difração de raios x e análise termogravimétrica. As misturas dos pós foram submetidas a prensagem uniaxial, utilizando uma pressão de compactação de 30 MPa num molde em forma de barra e estas foram sinterizadas a 1400ºC com uma taxa de aquecimento de 5ºC/min, permanecendo nesta temperatura durante 2 horas. Em seguida determinaram-se as propriedades físico-mecânicas tais como: retração linear de queima, absorção de água, porosidade aparente, massa específica aparente, tensão de ruptura à flexão em três pontos e microscopia eletrônica de varredura. Os resultados obtidos indicam que a mistura com mulita eletrofundida a 15%, promoveu um maior fechamento dos poros no material, causando assim um aumento na resistência mecânica em relação a mistura com alumina. A adição desse reforço inorgânico à matriz cerâmica (borra pura) demonstra um alto potencial de aplicação como matéria-prima para a indústria de materiais refratários conformados.
Abstract: White dross is a reject generated during aluminium production. It contains several oxides that can be useful to the refractories and cement industries. However, white dross can be hazardous both to human health and the environment. In this work, white dross was evaluated as a prospective raw material for the production of refractories. For this purpose, the dross was subjected to calcination followed by comminution and classification. In order to improve the mechanical properties of the refractory, two different kinds of electrofused particles were used separately as reinforcement: mullite and alumina. Particles of the TP-325 mullite were added to the white dross powder in proportions varying from 5 to 35% weight. The AL-L 280 alumina particles were added to another batch of refractories, in two different amounts (20 and 30% wt.). All materials were characterized by X-ray fluorescence, X-ray diffraction, and thermogravimetric analysis. Mixtures of residual powder and particles were compression molded as prismatic bars under a pressure of 30 MPa. Pressed bars were sintered in air at 1400ºC for 2h, and the heating rate was 5ºC/min. Mechanical and physical properties of the sintered parts were determined by means of linear shrinkage, water absorption, apparent porosity, density, MOR (three-point bending) and SEM analysis. The results obtained in this work indicate that the mixtures of white dross and 15% mullite allowed for a better compaction and density, producing parts with higher mechanical strength than the mixtures with alumina. Pyrometric cone tests at 1400ºC show the refractoriness of the parts up to that temperature. Therefore, under the conditions of this research work, white dross with additions of mullite particles has proven to be a prospective candidate for the production of refractory parts.
Descrição: MOTA, R. C. Influência da adição de cargas inorgânicas no desempenho de produtos refratários obtidos a partir de borras de alumínio. 2010. 112 f. Dissertação (Mestrado em Engenharia e Ciência de Materiais) - Centro de Tecnologia, Universidade Federal do Ceará, Fortaleza, 2010.
URI: http://www.repositorio.ufc.br/handle/riufc/1680
Aparece nas coleções:DEMM - Dissertações defendidas na UFC

Arquivos associados a este item:
Arquivo Descrição TamanhoFormato 
2010_dis_rcmota.pdf4,4 MBAdobe PDFVisualizar/Abrir


Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.