Title in Portuguese: Caracterização microestrutural e análise de textura cristalográfica do aço maraging 300 produzido por manufatura aditiva
Title: Microstructural characterization and crystallographic texture analysis of maraging 300 steel produced by additive manufacture
Author: Feitosa, Ana Larissa Melo
Advisor(s): Abreu, Hamilton Ferreira Gomes de
Keywords: Aços maraging
Manufatura aditiva
Textura cristalográfica
Título
Issue Date: 2017
Citation: FEITOSA, A. L. M. (2017)
Abstract in Portuguese: Os aços maraging são requisitados pelas indústrias, principalmente aeronáutica e naval, por sua resistência mecânica e tenacidade, além de boa resistência à corrosão e ductilidade. Mas seu grande diferencial está na capacidade de tornar-se mais resistente por meio de tratamentos térmicos de solubilização seguida de envelhecimento. As classes 300 e 350 desse aço são as mais difundidas, com isso, procura-se estudar e entender suas propriedades e desenvolver novas formas de produção desse material. Para isso, utilizou-se de aço maraging 300 produzido por manufatura aditiva, Direct Metal Laser Sintering (DMLS), o qual foi tratado e analisado em três estados: como recebido, solubilizado (820ºC/1h) e solubilizado/envelhecido (480ºC/5h). O material nos três estados foi submetido a difração de raios-x para produção de figuras de polo e FDOC’s, tornando possível a análise de macrotextura, microscopia óptica e eletrônica de varredura, possibilitando caracterização da microestrutura gerada pela técnica de fabricação, e microdureza, para verificação de efetividade dos tratamentos térmicos em comparação com o material como recebido. Verificou-se presença de fases dispersas de óxidos de Ti e Al nos três estados, além de ter-se verificado a diminuição da microdureza no estado solubilizado e o aumento no estado envelhecido, se comparado ao material como recebido.
Abstract: Maraging steels are required by industries, mainly aeronautics and naval, for their mechanical resistance and toughness, as well as good resistance to corrosion and ductility. But its great differential is in the ability to become more resistant through heat treatments of aging. As the classes 300 and 350 of steel are more widespread, with this, we try to find and understand their properties and develop new ways of producing this material. For this purpose, it was used maraging 300 produced by additive manufacture, Direct Metal Laser Signaling (DMLS), which was treated and analyzed in three states: as received, solubilized (820ºC/1h) and aged (480°C/5h). The material in the three states was subjected to X-ray diffraction for the production of poles and ODF, making possible a texture analysis, optical microscopy and scanning electron, making possible the characterization of the microstructure generated by the fabrication technique, and microhardness, for selection of effectiveness of thermal treatments in comparison to the material as received. There was presence of dispersed phases of Ti and Al oxides in the three states, in addition to the reduction of the solubilized state microhardness and increase in the aged state when compared to the material as Received.
Description: FEITOSA, Ana Larissa Melo. Caracterização microestrutural e análise de textura cristalográfica do aço maraging 300 produzido por manufatura aditiva. 2017. 51 f. Monografia (Graduação em Engenharia Metalúrgica) - Universidade Federal do Ceará, Fortaleza, 2017.
URI: http://www.repositorio.ufc.br/handle/riufc/29246
Appears in Collections:ENGENHARIA METALÚRGICA - Monografias

Files in This Item:
File Description SizeFormat 
2017_tcc_almfeitosa.pdf4,44 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.